WANG Mao-xiang, SUN Pin. FABRICATION AND HYSTERESIS LOOPS PROPERTY OF(Pb1-xSrx) TiO3 FERROELECTRIC THIN FILMS[J]. VACUUM AND CRYOGENICS, 2006, 12(3): 142-144.
Citation:
WANG Mao-xiang, SUN Pin. FABRICATION AND HYSTERESIS LOOPS PROPERTY OF(Pb1-xSrx) TiO3 FERROELECTRIC THIN FILMS[J]. VACUUM AND CRYOGENICS, 2006, 12(3): 142-144.
WANG Mao-xiang, SUN Pin. FABRICATION AND HYSTERESIS LOOPS PROPERTY OF(Pb1-xSrx) TiO3 FERROELECTRIC THIN FILMS[J]. VACUUM AND CRYOGENICS, 2006, 12(3): 142-144.
Citation:
WANG Mao-xiang, SUN Pin. FABRICATION AND HYSTERESIS LOOPS PROPERTY OF(Pb1-xSrx) TiO3 FERROELECTRIC THIN FILMS[J]. VACUUM AND CRYOGENICS, 2006, 12(3): 142-144.
FABRICATION AND HYSTERESIS LOOPS PROPERTY OF(Pb1-xSrx) TiO3 FERROELECTRIC THIN FILMS
The（Pb1-xSrx）TiO3 thin films were prepared by magneticsputtering technology.The hysteresis loo ps property of PST thin films was measured and analyzed.The saturated polarization intensity,the residual polarizat ion intensity and the coercive electric field of the PST sample were about 19.0 μC/cm2,6.6 μC/cm2 and 16 kV/cm,respectively.The pyroelectric coefficient was in 10-4 order.